1. Compared with that of limestone, the properties of siliceous material will have more influence on the burnability of raw meal.
   与石灰石相比，硅质原料性质对生料易烧性影响更大。
2. This paper is concerned with the effect of foreign oxides on the burnability of cement raw meal with high CaO.
   本文比较了外掺各种氧化物对高钙生料易烧性的影响规律。
3. It is possible to improve the burnability and to increase clinker strength by admixing ions in single or complex way.
   一些杂质离子单独或复合使用，能够改善熟料易烧性，提高熟料的强度。
4. The result shows that microstructure of clinker is various from different grinding system, and their burnability is also various.
   研究表明，不同粉磨系统的生料其微观结构有差异，易烧性也有差别。
5. The result shows that the burnability of cement raw meal with high content of C3S batching was improved with suitable content of phosphor slag, but the effect of copper slag and lead-zinc slag was not that obvious.
   研究表明：铜渣、铅锌渣对改善高C3S配料的水泥生料易烧性效果不明显，掺入适量磷渣可很好地改善水泥生料的易烧性。
6. Study on the Improvement of Burnability of Cement Raw Meal with Yellow-Sand or Shale
   利用黄沙或页岩配制的水泥生料易烧性的改善研究
7. The Influences of adding different mineralizers on burnability of Portland cement raw meals, mineral composition and petrographic structure of cement clinker were studied in this paper.
   研究了在水泥生料中掺入不同矿化剂对水泥生料的易烧性、硅酸盐水泥熟料矿物形成和岩相结构的影响。
8. Study on effect of property of limestone on burnability of meal
   石灰石品质对生料易烧性影响的研究
9. The effect of Cr-slag on burnability of cement raw materials, liquid phase appearance temperature of cement clinker burning and physical properties of cement clinker were studied.
   研究了铬渣对水泥生料易烧性、熟料烧成液相出现温度及熟料物理性能的影响；
10. The burnability of the high tricalcium silicate Portland cement raw meal produced by lead-zinc tailing and shale and property of the resulting clinker were studied in this work.
    研究了采用铅锌尾矿和页岩配制的高C3S硅酸盐水泥生料的易烧性及所得熟料的性能。
11. The experiment in decomposition kiln using steel slag to replace iron powder was carried out, the results showed that steel slag can improve the burnability of the green materials and obtain obvious economic benefit.
    在预分解窑进行了钢渣代替铁粉配料的试验，结果表明，钢渣配料可以提高生料的易烧性，并取得明显的经济效益。
12. This paper studies the influences of copper tailings on the burnability of cement raw meal and on cement strength when copper tailings are used to replace iron cinders wholly and clay and limestone partly in the mix.
    本文研究了利用铜尾矿全代铁粉和部分取代粘土、石灰石配料时，铜尾矿对水泥生料易烧性及水泥强度的影响。
13. The burnability of the cement raw meal prepared by shale or yellow-sand has been studied in this paper.
    本文研究了以黄沙或页岩代替粘土质原料配制水泥生料的易烧性。
14. Effect of grinding methods on characteristic and burnability of raw meal
    粉磨方法对生料特性及生料易烧性的影响
15. Effect of additive crystal seed on burnability of Portland cement raw meals
    添加晶种对硅酸盐水泥生料易烧性影响的研究
16. The results reveal that the grindability and burnability of raw meal, the quality and output of clinker as well as the setting time of clinker can be improved with the addition of phosphorus gypsum.
    结果表明，用磷石膏配料，能改善生料的易磨性和易烧性，提高生、熟料的产量，并能改善熟料的凝结特性。
17. Study on improving the burnability of cement raw meal made with sandstone
    提高砂岩配料生料易烧性的研究
18. Using burnability index to control the burning temperature of rotary kiln
    用生料易烧性指数控制回转窑煅烧温度
19. Burnability of raw meal with selected formula was improved by using copper and zinc tailing and tin slag as raw materials.
    利用铜锌尾矿和锡渣双掺配料，选用较佳的配方，改善了生料的易烧性；
20. The chemical analysis, laser granulometer and SEM was used to study the characteristic and burnability of raw meal prepared by ball mill and vertical mill in JIDONG CEMENT CO.
    采用了化学分析、激光粒度分析、扫描电镜等手段，对冀东水泥股份有限公司球磨和立磨制备的生料特性及生料易烧性进行了研究。
21. Effects of the Amount of Solvent Minerals and Alumina Ratio on Cement Raw Material Burnability
    熔剂性矿物的数量和铝率对生料易烧性的影响
22. The results reveal that the main factor which influences the burnability is the grain size of crystal quartz.
    结果表明，硅质原料中对生料易烧性产生影响的首要因素是石英晶体的大小。
23. The results show that alkalis in the waste liquid can reduce burnability of raw meal and the strength of cement was reduced in various age.
    结果表明，纸浆废液中的碱使生料的易烧性降低，使水泥各龄期强度降低；
24. A research has been made on the effects of the grain size, crystallinity and quantity of crystal quartz in siliceous raw material on the burnability of cement raw meal.
    研究了硅质原料中石英晶体大小、相对结晶度及数量对水泥生料易烧性的影响。
25. In this paper, various kinds of monomineral, pure clinker and white cement clinker, prepared in laboratory are used as crystal seeds. Effects of the above crystal seeds on burnability of OPC raw meal are studied by means of DTA, XRD and free lime measurement.
    采用实验室制备的不同种类单矿物、纯熟料及白水泥熟料为晶种，利用DTA，XRD及测定游离石灰等方法，研究了其对普通硅酸盐水泥生料易烧性的影响。
26. The lead-zinc slag can also significantly improve the burnability of the raw meal, dropping liquid phase appearance temperature of clinker burning and promote the absorption of free lime ( f-CaO) and the formation of silicate minerals.
    铅锌渣能够显著改善生料易烧性，降低液相出现温度，促进游离氧化钙（f-CaO）吸收和硅酸盐矿物形成。
27. The research results indicate that steel slag can substitute for iron ore to be used to product clinker, which can also significantly improve the burnability of raw meal and reduce energy consumption.
    研究结果表明：钢渣可以替代铁矿石进行配料生产硅酸盐水泥熟料，还能显著改善生料易烧性、降低熟料烧成热耗。
28. The application of phosphorus slag ( PS) in the cement industry has two aspects, one is used as raw materials for cement clinker producing to improve the burnability; secondly, it can be used as cement admixture.
    磷渣在水泥工业中的应用有两方面，一方面是作为原料生产水泥，可以改善生料的易烧性。另一方面，可以作为水泥混合材。
29. The research results indicate that FS mineralization can significantly improve the burnability of the raw material and lower sintering temperature.
    实验结果表明：FS矿化剂能够显著改善生料易烧性，大大降低熟料烧成温度。
30. Shale could improve the raw material burnability, which had good for formation of cement minerals.
    页岩可改善生料的易烧性，有利于水泥矿物的形成。