chromizing
英
美
n. 渗铬（处理）；铬化（处理）；扩散镀铬
双语例句
- Preparation and Oxidation Performance of an-Al_2O_3-Modified Chromizing Coating
Al2O3改性的渗铬涂层制备与氧化性能研究 - Technic and Performance of Steel 20 Treated by Low-temperature Chromizing in Salt-bath Scaling control and removal for extra-low permeability reservoir in Jiyuan Oilfield
20钢低温盐浴渗铬工艺及性能研究姬塬特低渗高含盐地层结垢防治效果 - The results show that after deposition of diamond between 600 ℃ and 900 ℃, the thick of chromium-carbon compounds layers and chromizing layers increase;
结果发现，以渗铬层为基底在600～900℃之间进行CVD金刚石薄膜沉积后，渗铬层的铬碳化合物层和铬扩散层的厚度都增加了； - Surface chromizing at900 ℃ of T8 steel was studied using double glow plasma alloying process.
采用双辉等离子渗铬技术，对T8钢进行了900℃温度表面渗铬合金化； - The surface micrographs and phase structure in chromizing layer were analyzed.
分析了渗铬改性层的表观形貌和相结构，测量了渗铬改性层的成分。 - Effect of salt-bath chromizing process on microstructure and properties of chromized layer
T12钢盐浴渗铬工艺对渗层组织和性能的影响 - The ionic chromizing of steel is done by means of ionitriding furnace.
利用离子氮化炉进行钢的离子渗铬。 - Study on Improving Wear-resistance of Steel by Plasma Chromizing and Compound Strengthening
等离子渗铬及复合强化处理提高耐磨性能的研究 - Effect of Chromizing on Properties of Liquid Forming Die
渗铬对液态成型模具用钢性能的影响 - Thermodynamic Analysis of Carbon Migration during T 8 Steel during Plasma Surface Chromizing
表面渗铬T8钢中碳迁移的热力学分析 - Compared with the chromizing layer, the chromosiliconizing layer on cast iron is more unifomrm and more compact.
与单纯渗铬层相比，铸铁铬硅共渗层的连续性和致密性有所增强。 - Test Study on Plasma Paste Chromizing
等离子体膏剂渗铬的试验研究 - The test results indicate that the hardness and wear resistance depend on the chromium carbide and σ phase which are distributed in the chromizing layer.
渗铬层中形成的铬碳化物明显提高了表面硬度和耐磨性，同时σ相的存在也是渗层具有高硬度的重要原因。 - The separation and determination of Cr~ 0, crcl_2, crcl_3 and cr_2o_3 in the molten salts for chromizing
渗金属融盐中Cr~0，CrCl2，CrCl3及Cr2O3的分离与测定 - Researches on New Technology of Chromizing with Neutral Salt Bath
中性盐浴渗铬新工艺的研究 - Wear-Resistant Alloying Layer of Plasma Surface Chromizing and Carburizing
等离子表面渗铬渗碳耐磨合金层 - Morphology and surface stress of ionic chromizing coating of steel
钢的离子渗铬层组织及表面应力研究 - This paper deals with the salt bath chromizing techniques and the effect of RE as a catalytic agent in salt bath on T12A steel chromizing technique, layer microalloying, structure and properties.
研究了熔盐被覆铬碳化物的工艺过程，着重探讨了稀土对T12A钢熔盐渗铬的催渗及微合金化作用机理。 - Low Temperature Double Glow Plasma Surface Chromizing Hardening Process of Carbon Tool Steel
碳素工具钢表面低温双辉等离子渗铬硬化的研究 - By observing and analyzing the casting test piece, we have found a metallurgical integrating layer that is made up of chromizing cast-iron alloy layer.
我们还对铸渗质量较好的铸渗试件进行了观察和分析，发现铸铁渗铬合金层与母材结合良好，呈冶金结合。 - Research on Glow Ionic Chromizing of Steel
钢的辉光离子渗铬研究 - Under controlling technique factors, we have produced high quality chromizing cast-infiltration layer.
通过控制工艺因素，在铸铁件表面获得了质量完好的铸渗层。 - Paste ion chromizing by ion nitriding furnace was introduced.
利用普通离子渗氮炉进行了膏剂离子渗铬。 - During electrokinetic measurement and salt immersion test, the chromizing layer shows passive behavior and good corrosive resistance.
在动电位极化曲线测试中，渗层表现出明显的钝化行为，并在盐水浸泡实验中表现出良好的耐蚀性。