disaccommodation

英

美

网络磁导率减落; 减落; 不匹配

The dependence of disaccommodation on temperature shows that it is a comprehensive effect of the ordering effect of atoms 'orientation with stress relaxation.
减落随温度的变化是原子方向有序和应力松弛的综合效应。
As revealed, the influence of alloy composition on disaccommodation is resulting from the magnetostriction which couples the structural defects with magnetization.
表明合金成分对减落的影响是由于结构缺陷与磁化强度的磁致伸缩耦合的结果。
The most probable activation energies for disaccommodation and decay are about 1.0 eV and 1.4 eV, respectively.
普通减落和磁导率衰减过程的最可几激活能分别为1.0eV和1.4eV。
Based on this mechanism, a new relaxation law of magnetization and a new formula of magnetic disaccommodation were derived.
在此新机制的基础上，导出了分指数的磁化强度弛豫规律和磁导率减落公式。
Disaccommodation of initial susceptibility in amorphous fe_ ( 90-x) ni_xzr_ ( 10) alloys
非晶态Fe（90-x）NixZr（10）合金的起始磁化率减落
It was found that the disaccommodation measured at low temperature range is a monotonically decreasing function of Fe content. However, a peak of disaccommodation was observed at higher temperature range.
发现在较低温度下，减落随Fe含量减少单调下降，而在较高的温度，则观察到一个减落峰。